BONDERITE® S-FN 310 (also known as Emralon 309) is a phenolic resin-bonded PTFE coating for long-term lubrication at high temperatures on a wide range of surface types.  BONDERITE® S-FN 310 provides a uniform surface coating that exhibits incredible wear protection & operational life that outperforms conventional PTFE solutions.

BONDERITE® S-FN 310 is a powerful dry-film solution for long term protection in a wide range of applications.  BONDERITE® S-FN 310 is provided as a two-part system, that is mixed upon time of application – slowly add component “A” to component “B” with continuous stirring for homogeneity. 
 
The mixed BONDERITE® S-FN 310 solution is then sprayed onto the surface in a thickness between 0.2 - 0.7 mils, or 4 – 6 passes with the spray nozzle.  The shelf life of the prepared mixture is 24 hours.
 
Once the coating is applied, allow the surface to dry (5-10 minutes) before loading into curing oven.  The most popular curing cycles and temperatures based on an average coating of 0.0003 inch and are listed below:
 
60 minutes at 300°F (149°C)
10 minutes at 350°F (177°C)
8 minutes at 400°F (204°C)
4 minutes at 500°F (149°C)
 

Extended-term PTFE Protection
Multi-purpose Lubricating Solution
Excellent Adhesion on Multiple Surface Types (Wood, Steel, Aluminum, Copper Alloys, Rubber, Plastics)

BONDERITE® S-FN 310 helps provide a solution to the following industry & application problems: 
 
Inefficient PTFE or Protective Coating Lifespan
Dry-Film Breakdown at High Temperatures

Package: 2 components ready for mixing (typical)
Color: light green (cured)
Density, as applied: 8.2 lb./gal
Density, “A” Component: 13.0 lb./gal
Density, “B” Component: 7.5 lb./gal
Consistency: Liquid
Service Temperature: 350°F (177°C)
Intermittent Temperature: 400°F (204°C)
Flash Point: 46°F (9°)